@article{Hai Van_Nam_Thom_Phuong_Xuan Hang_Mai Thanh_2017, title={Synthesis, characterization and corrosion inhibitive ability of composites silica – polypyrrole}, volume={55}, url={https://vjst.net/index.php/vjchem/article/view/2525-2321.2017-005343}, DOI={10.15625/2525-2321.2017-005343}, abstractNote={<p>Composites silica/polypyrrole (SiO<sub>2</sub>/PPy) were synthesized by in-situ, using FeCl<sub>3</sub> as oxidant, the quantity of silica is varied from 0.15 g, 0.3 g, 0.45 g to 0.6 g (SP1, SP2, SP3 and SP4, respectively). The morphologies and characterizations of composites were evaluated by FT-IR, EDX, SEM, TEM and TGA. EDX result indicated that the percentage of silicon increase from 20.48 to 28.14 % when the quantities of silica in initial mixture increase. Carbon steel were coated with polyninylbutyral (PVB) resin and PVB coatings containing 10 % SP1, SP2, SP3 and SP4 by spin coating technique. Corrosion protection performance of PVB coating containing SiO<sub>2</sub>/PPy was evaluated by measurement of OCP and potentiodynamic polarization.  The results shows that the SiO<sub>2</sub>/PPy in PVB coating has corrosion inhibitive ability for carbon steel, it can shift the potential of steel into anode areas and reduce the corrosion current density more than 100 times.</p> <p><strong>Keywords.</strong> Composite silica-polypyrrrole, corrosion inhibitive ability, corrosion performance.</p>}, number={6}, journal={Vietnam Journal of Chemistry}, author={Hai Van, Vu Thi and Nam, Pham Thi and Thom, Nguyen Thi and Phuong, Nguyen Thu and Xuan Hang, To Thi and Mai Thanh, Dinh Thi}, year={2017}, month={Dec.}, pages={781} }