PHẢN ỨNG GHÉP GLYCIDYLMETACRYLAT LÊN POLYETYLEN PHẦN I. ẢNH HƯỞNG CỦA CÁC YẾU TỐ CÔNG NGHỆ ĐẾN PHẢN ỨNG GHÉP


Authors

  • Nguyễn Thị Thuỷ
  • Nguyễn Huy Tùng
  • Bùi Chương
DOI: https://doi.org/10.15625/2258

Abstract

Grafting reactions of glycidylmethacrylate on polyethylene were carried out in a Brabender internal mixer with capacity of 50 ml. There are strong and sharp peak in the PE-g-GMA IR spectra at about 1730 cm-1corresponding to carbonyl group (C=O) and at 850 và 910 cm-1corresponding epoxy group, but these peaks have not seen in neat PE spectra. The parameters of process condition were selected to achieve the highest grafting content: the temperature at 185oC, rotor speed of 40 rpm for 11 min. The received PE-g-GMA possessed: grafting content 1.705 wt.%, melt flow index 5.27 g/10 min and contact angle  45.21o.

Downloads

Download data is not yet available.

Downloads

Abstract View: 97
PDF Downloaded: 25

Published

15-08-2012

How to Cite

Thuỷ, N. T., Tùng, N. H., & Chương, B. (2012). PHẢN ỨNG GHÉP GLYCIDYLMETACRYLAT LÊN POLYETYLEN PHẦN I. ẢNH HƯỞNG CỦA CÁC YẾU TỐ CÔNG NGHỆ ĐẾN PHẢN ỨNG GHÉP. Vietnam Journal of Chemistry, 49(2). https://doi.org/10.15625/2258

Issue

Vol. 49 No. 2 (2011)

Section

Articles