Nghiên cứu chế tạo vật liệu polyme phân hủy sinh học trên cơ sở nhựa polypropylen gia cường bằng sợi nứa. Phần 1. Ảnh hưởng của nồng độ dung dịch tới hiệu ứng tổng trở khổng lồ


Authors

  • Trần Vĩnh Diệu và cộng sự
DOI: https://doi.org/10.15625/4464

Abstract

Neohouzeaua dullooa fibers were prepared by mechanical method. Its composition and morphology of fibers were studied. The analytical result shown that, most of hemicelluloses and lignin were removed. FTIR spectroscopy shows that strong sharp peak in the untreated bamboo spectrum at about 1736 cm-1corresponding to carbonyl group (>C=O), but this peak disappeared in alkaline treated bamboo spectrum. Bamboo fiber reinforced polypropylene grafted maleic anhydride composites have been prepared by 50% fiber contents. The mechanical properties of composite were also tested.

Downloads

Download data is not yet available.

Downloads

Abstract View: 107
PDF Downloaded: 45

Published

19-08-2014

How to Cite

Diệu và cộng sự, T. V. (2014). Nghiên cứu chế tạo vật liệu polyme phân hủy sinh học trên cơ sở nhựa polypropylen gia cường bằng sợi nứa. Phần 1. Ảnh hưởng của nồng độ dung dịch tới hiệu ứng tổng trở khổng lồ. Vietnam Journal of Chemistry, 46(4), 493. https://doi.org/10.15625/4464

Issue

Vol. 46 No. 4 (2008)

Section

Articles